dc.description.abstract | El presente trabajo de investigación se enfoca en el estudio experimental de la adición
porcentual de diatomita en estado calcinado al concreto F’c: 210 Kg/cm2, con la finalidad de
determinar en que difiere la resistencia a la compresión axial, el desarrollo de la temperatura
en estado fresco y consistencia del mismo, adicionado con diatomita en estado calcinado con
respecto de un concreto patrón.
Para tal efecto, en la presente investigación se elaboró 72 briquetas de concreto F’c: 210
Kg/cm2 de resistencia a la compresión y concreto adicionado porcentualmente con diatomita
en estado calcinado en 5%,10% y 15%; posteriormente se realizó los ensayos de compresión
axial a las muestras para determinar la resistencia y evolución de los mismos en el tiempo, así
como realizar ensayos de temperatura y consistencia del concreto patrón y adicionado en estado
fresco.
Y contando con los resultados obtenidos se determinó que la resistencia a la compresión axial
en probetas- testigo de concreto de diseño F’c: 210 Kg/cm2 incrementa significativamente su
resistencia, así como la diatomita se comporta como acelerante de fragua del concreto por
elevar la temperatura del mismo en estado fresco.
Capítulo I: Planteamiento del problema
A la presente fecha se tiene registro y/o conocimiento limitado respecto de un mejor desempeño
del concreto F’c: 210 kg/cm2 adicionado con diatomita en estado calcinado en la ciudad del
Cusco, como así lo demuestra los antecedentes locales contenidos en la presente tesis.
La adición de este nuevo material al concreto incrementaría la resistencia a la compresión axial
y reduciría el costo económico por metro cubico producido, reduciendo la cantidad de cemento
utilizado en la elaboración de concreto, también se activaría la economía en los alrededores de
los posibles yacimientos a explotar.
Capítulo II: Marco teórico
Presentamos los antecedentes tomados en cuenta en la presente investigación relacionada con
el tema de estudio también, elegimos un autor y/o norma que tenga la capacidad de explicar y
medir nuestros datos como lo es la NTP, Sirve para interpretar los datos, son un esquema
explicativo para poder hacer el contraste con los datos que encontraste en la realidad para poder
interpretarlo desde el enfoque técnico teórico. Capítulo III: Metodología
En el presente capítulo se aborda el tipo, nivel y el método de la investigación, así como
también se indica el diseño de la investigación, la población y la muestra los instrumentos
metodológicos o de recolección de datos e instrumentos de ingeniería, los procedimientos de
recolección, análisis de datos y el diseño de ingeniería o flujograma de los trabajos realizados.
Capítulo VI: Resultados
Se utilizó la NTP. En cuanto a la realización de todos los ensayos necesarios para los agregados
finos, gruesos, necesarios para el diseño de mezcla de concreto y ensayos en cuanto a rotura de
briquetas, temperatura y revenimiento del mismo, para posteriormente presentar las tablas y
gráficos conteniendo los resultados de la presente investigación.
Capítulo V: Discusión
En el presente capítulo se realizó un contraste en cuanto a similitudes y diferencias de los
resultados y hallazgos obtenidos en la presente investigación con el marco teórico,
antecedentes. | es_PE |
dc.description.abstract | The present research work focuses on the experimental study of the percentage addition of
calcined diatomite to concrete F'c: 210 Kg/cm2, in order to determine the differences in axial
compressive strength, temperature development in fresh state, and consistency of the same,
added with calcined diatomite with respect to a standard concrete. For this purpose, in the
present research, 72 concrete F'c: 210 Kg/cm2 strength briquettes with percentage addition of
calcined diatomite at 5%, 10%, and 15% will be prepared; subsequently, axial compression
tests will be carried out on the samples to determine their strength and evolution over time, as
well as temperature and consistency tests of the standard and added concrete in fresh state. And
based on the results obtained, it was determined that the axial compressive strength in control
concrete test specimens of design F'c: 210 Kg/cm2 significantly increases its strength, and
diatomite behaves as an accelerating agent of concrete setting by increasing its temperature in
the fresh state.
Chapter I: To date, there is a record and/or limited knowledge regarding a better performance
of concrete F'c: 210 kg/cm2 added with diatomite in a calcined state in the city of Cusco, as
demonstrated by the local information contained in this document. thesis.
The addition of this new material to the concrete would increase the resistance to axial
compression and would reduce the economic cost per cubic meter produced, reducing the
amount of cement used in the preparation of concrete, it would also activate the economy in
the surroundings of the possible deposits to blow
Chapter II: Theoretical framework We present the background taken into account in the
present research related to the study topic as well, we chose an author and/or standard that has
the ability to explain and measure our data such as the NTP. It serves to interpret the data. They
are an explanatory scheme to be able to contrast the data found in reality in order to interpret it
from the technical-theoretical approach.
Chapter III: Methodology In this chapter, the type, level, and method of research are addressed,
as well as the research design, population and sample, methodological or data collection
instruments, and engineering instruments, data collection procedures, data analysis, and the
engineering design or flow chart of the work performed.
Chapter VI: Results the NTP was used. Regarding the performance of all necessary tests for
fine and coarse aggregates, necessary for the design of concrete mix and tests on the rupture of briquettes, temperature, and Slump of the same, to subsequently present the tables and graphs
containing the results of the present research. Chapter V: Discussion In this chapter, a contrast
was made regarding the similarities and differences of the results and findings obtained in the
present research with the theoretical framework and background. | en_US |
dc.format | application/pdf | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Andina del Cusco | es_PE |
dc.rights | info:eu-repo/semantics/openAccess | es_PE |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | es_PE |
dc.subject | Diatomita | es_PE |
dc.subject | Resistencia a la compresión axial | es_PE |
dc.subject | Revenimiento y temperatura | es_PE |
dc.title | Evaluación de la resistencia a la compresión axial del concreto f’c: 210 kg/cm2, elaborado con adiciones porcentuales de 5%, 10% y 15% de diatomita en estado calcinado con respecto a un concreto patrón a los 7, 14 y 28 días de curado | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.name | Ingeniero Civil | es_PE |
thesis.degree.grantor | Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura | es_PE |
thesis.degree.discipline | Ingeniería Civil | es_PE |
dc.publisher.country | PE | es_PE |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.01.00 | es_PE |
renati.advisor.dni | 25001820 | |
renati.advisor.orcid | https://orcid.org/0000-0002-3256-7664 | es_PE |
renati.author.dni | 23999677 | |
renati.discipline | 732016 | es_PE |
renati.juror | Alvarez Espinoza, Jorge | |
renati.juror | Arohuanca Sosa, Rode Luz | |
renati.juror | Rios Rabelo, Jose Luis | |
renati.juror | Gonzales Mamany, Nico Yheison | |
renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | es_PE |
renati.type | https://purl.org/pe-repo/renati/type#tesis | es_PE |