dc.description.abstract | La presente tesis se enmarca en la ciudad de Cusco, la investigación fue orientada al estudio de las propiedades de compresión y flexión de muestras de mortero f‟c= 125 kg/cm2 y f‟c= 175 kg/cm2 con adición de hilo macramé tipo clave 12 y fibras de polipropileno Sikafiber®PE en porcentajes de 0.25%,0.50% y 1.00%, medidas en porcentajes de peso de cemento, la mezcla de mortero se
fabricó con arena fina de Pisac, arena fina de Cunyac y cemento Portland tipo IP, y la comparación de estas con muestras de mortero f‟c= 125 kg/cm2 y f‟c= 175 kg/cm2 sin adicción, los ensayos fueron realizados a edades de 3,7,14 y 28 días.
El diseño de mortero f‟c= 125 kg/cm2 y f‟c= 175 kg/cm2 se elaboró con una metodología colombiana, al realizar la mezcla de mortero se verificó los parámetros del flujo de diseño y se realizó una verificación posterior a la adición de hilo macramé tipo clave 12 y fibras de polipropileno Sikafiber®PE en porcentajes de 0.25%, 0.50% y 1.00%, con la mezcla obtenida se elaboró muestras cúbicas de 5 cm de lado para ensayos de compresión y muestras prismáticas de 4cm*4cm*16cm para ensayo a flexión.
De acuerdo con los resultados, el mortero adicionado con fibras de polipropileno Sikafiber®PE, mejoran la de resistencia a compresión de un mortero f‟c= 175 kg/cm2 siendo mayor en un mortero f‟c= 125kg/cm2, lo cual es contrario con las propiedades de flexión que se ven reducidas en un
mortero f‟c= 125 kg/cm2 y f‟c= 175 kg/cm2 en todos los porcentajes del empleo de fibras de polipropileno. El mortero adicionado con hilo macramé clave 12, reduce la resistencia a compresión de un mortero f‟c= 175 kg/cm2, en el caso de un mortero f‟c= 125 kg/cm2 le incrementa solo el porcentajes de 0.25% y posteriormente empieza a descender, la resistencia a flexión se ve reducida en un mortero f‟c= 175 kg/cm2 y se incrementa en un mortero 125kg/cm2, al adicionar hilo macramé. | es_PE |
dc.description.abstract | This thesis is part of the city of Cusco, the research was aimed at studying the properties of compression and bending of mortar samples fc = 125 kg / cm2 and fc = 175 kg / cm2 with the addition of macramé thread key 12 and polypropylene fibers Sikafiber®PE percentage of 0.25%, 0.50% and 1.00%, measured in percentages by weight of cement, mortar mix was manufactured Pisac fine sand, fine sand and Portland cement Cunyac type IP, and comparing these with mortar samples fc = 125 kg / cm2 and fc = 175 kg / cm2 without addiction, the tests were conducted at ages 3,7,14 and 28 days.
.
The design of mortar fc = 125 kg / cm2 and fc = 175 kg / cm2 was developed with a Colombian methodology when mixing mortar flow parameters design was verified and further verification was carried out at the macramé yarn addition key 12 and polypropylene fibers in percentages Sikafiber®PE 0.25%, 0.50% and 1.00%, with the obtained mixture type cubic samples of 5 cm side and compression testing prismatic samples was prepared 4cm * 4cm * 16cm for bending test.
According to the results, mortar with polypropylene fibers added Sikafiber®PE, improve the compressive strength of a fc = 175 kg / cm2 in a mortar being greater fc = 125kg / cm2 mortar, which is contrary to the bending properties that are reduced in a f'c = 125 kg / cm2 and f'c = 175 kg / cm2 mortar. The mortar added with key macramé thread 12 reduces the resistance to compression of f'c
= 175 kg / cm2 mortar, in the case of f'c = 125 kg / cm2 mortar will only increase percentages of 0.25% and subsequently begins to descend, the flexural strength is reduced in a f'c = 175 kg / cm2 and mortar is increased 125kg / cm2 mortar. | en_US |
dc.description.uri | Tesis | es_PE |
dc.format | application/pdf | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Andina del Cusco | es_PE |
dc.rights | info:eu-repo/semantics/restrictedAccess | es_PE |
dc.source | Universidad Andina del Cusco | es_PE |
dc.source | Repositorio Institucional - UAC | es_PE |
dc.subject | Mortero | es_PE |
dc.subject | Hilo macramé | es_PE |
dc.subject | Compresión | es_PE |
dc.subject | Flexión | es_PE |
dc.title | Análisis del desarrollo comparativo de la resistencia a compresión y flexión de un mortero (C:A) F`C=125kg/cm2 y F`C=175 kg/cm2 elaborado con agregados de Pisac y Cunyac adicionado con hilo macramé y fibras de polipropileno. | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.name | Ingeniero Civil | es_PE |
thesis.degree.grantor | Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura | es_PE |
thesis.degree.level | Titulo Profesional | es_PE |
thesis.degree.discipline | Ingeniería Civil | es_PE |