dc.description.abstractEn la presente tesis se realizó la evaluación comparativa del mortero de cemento Tipo I y mortero con el reemplazo del cemento Portland Tipo I en peso por puzolana de la cantera de Ccocha, con respecto al cemento Pórtland Tipo IP, realizando distintos ensayos, todos respetando las NTP, RNE, MTC y ASTM, para los ensayos. Gratamente se ha obtenido que a los 28 días de edad, la resistencia a la compresión, flexión y adherencia, del mortero elaborado con reemplazo de 28% de la puzolana, “supera a los patrones”; sin embargo en la fluidez se aprecia “disminución” de la misma. Se evaluó los resultados del análisis de laboratorio de la puzolana de la cantera de Ccocha, que muestran porcentajes adecuados para ser empleados como cemento puzolánico, se aprecia la reactividad al cemento tipo I a partir del 28% de reemplazo de la puzolana disminuyendo en su resistencia mecánica y el resultados del índice de actividad puzolánica es de“143.74% siendo éste mayor a la norma NTP 334.090 que nos indica como mínimo 75%”. Posteriormente se evaluó los pesos específicos de los cementos tipo I, IP y reemplazado con el cemento Portland Tipo I por puzolana de la cantera de Ccocha en porcentajes de 15%, 28% y 40% (experimental).Los resultados “cumplen con la norma ASTM C 188-95, que indica entre 2.9 a 3.15 gr/cm3. Así como también se puede observar en el gráfico N° 08, que a 28 % el peso específico es igual al patrón tipo IP”. Posteriormente se evaluó la fluidez del mortero, que “a mayor porcentaje de reemplazo de Tipo I por la puzolana de la cantera de Ccocha, la fluidez disminuye con relación al patrón Tipo IP. Así como también se puede apreciar en el gráfico N° 02, que cuanto mayor es la relación a/c es mayor la fluidez en el mortero”. Seguidamente se evaluó la resistencia a la compresión de los morteros de cemento Portland Tipo I, IP y experimental, mediante cubos de 5 cm de lado, sometidos a una fuerza constante de compresión en los cuales se cumplieron con la NTP 334.051, concluyendo que “a los 28 días de las muestras (cubos), el mortero elaborado con reemplazo de 28% de puzolana, alcanza una resistencia de 36.37MPa, que es un valor mayor que el patrón”. Así como también se evaluó la resistencia a la flexión de los morteros de cemento Portland Tipo I, IP y experimental, mediante prismas de 4cmx16cmx4cm, concluyendo que “a los 28 días de las muestras prismáticas, el mortero elaborado con reemplazo de 28% de puzolana, alcanza una resistencia de 8.83 MPa, que es un valor mayor que el patrón”. Posteriormente se evaluó la resistencia a la flexión por adherencia, mediante muestras prismáticas que consisten de 5 unidades de albañilería (pilas), realizadas con cemento Portland Tipo I, IP y experimental, los cuales se cumplieron con la NTP 334.129, concluyendo que “a los 28 días de las muestras prismáticas (pilas), el mortero elaborado con reemplazo de 28% de puzolana, alcanza una resistencia de 10.31 Kgf/cm2, más que el patrón elaborado con cemento Portland tipo IP que llega a 9.27 Kgf/cm2, de esa manera superando en 1.04 Kgf/cm2”.es_PE
dc.description.abstractIn this thesis benchmarking cement mortar and mortar type I was performed withreplacement of Type I Portland cement with pozzolan quarry Ccocha with respectto Portland cement IP, performing various tests, all respecting the NTP, RNE,MTC and ASTM, for testing. Pleasantly was obtained at 28 days of age, the bending adhesion, resistance tocompression and bending of mortar prepared with replacement of 28% of thepozzolan, “exceeds employers“ however fluency seen “ decline “of it. The results of laboratory analysis of the gravel quarry Ccocha, showingpercentages suitable for use as a pozzolan cement was evaluated reactivity cement type I appreciated from 28% pozzolan replacement decreasing in itsresistance mechanics and results pozzolanic activity index is “this being 143.74% higher than the NTP standard 334.090 which indicates at least 75%”. Subsequently the specific weights of type I cements, IP and replacements Type I Portland cement with pozzolan quarry Ccocha percentage of 15%, 28% and 40% (experimental) was evaluated. The results “comply with ASTM C 188-95 standard,which indicates between 2.9 to 3.15 g/cm3. As can also be seen in Figure No. 08,28% specific weight is equal to the rate IP standard”. Then the compressive strength of cement mortars Portland Type I, IP andexperimental assessed by cubes of 5 cm side , under constant compressive forcewhich met with the NTP 334,051 , concluding that “28 days of the samples (blocks) , the mortar prepared with 28 % replacement pozzolan , reaches aresistance of 36.37 MPa , which is a value greater than the standard“. And the flexural strength of Portland cement mortars Type I, IP and experimentalthrough prisms 4cmx16cmx4cm , concluding also assessed that “after 28 days ofthe prismatic sample , mortar made with replacement of 28 % pozzolan reaches8.83 MPa resistance , which is a value greater than the standard“. Subsequently, the flexural strength of adhesion was evaluated by prismaticsamples consisting of 5 masonry units (batteries), made with Portland cement Type I, IP and experimental, which complied with the NTP 334 129, concluding that “the 28 days of age of the batteries, prismatic samples, mortar made with Portland cement type I and 28% replacement of pozzolan gives us the best resistance with an increase of 1.04 kgf / cm2 but the pattern made with Portland cement mortar IP type“.en_US
dc.description.uriTesises_PE
dc.formatapplication/pdfes_PE
dc.language.isospaes_PE
dc.publisherUniversidad Andina del Cuscoes_PE
dc.rightsinfo:eu-repo/semantics/restrictedAccesses_PE
dc.sourceUniversidad Andina del Cuscoes_PE
dc.sourceRepositorio Institucional - UACes_PE
dc.subjectMorteroes_PE
dc.subjectPuzolanaes_PE
dc.subjectAdherenciaes_PE
dc.subjectFluidezes_PE
dc.titleEvaluación comparativa de la fluidez, peso específico, adherencia, resistencia a la compresión y flexión de mortero elaborado con cemento Portland Tipo IP y tipo I con el reemplazo del cemento Portland Tipo I por Puzolana de la cantera de Ccocha - San Pedro Sicuani - Cusco.es_PE
dc.typeinfo:eu-repo/semantics/bachelorThesises_PE
thesis.degree.nameIngeniero Civiles_PE
thesis.degree.grantorUniversidad Andina del Cusco. Facultad de Ingeniería y Arquitecturaes_PE
thesis.degree.levelTitulo Profesionales_PE
thesis.degree.disciplineIngeniería Civiles_PE


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record