dc.description.abstract | La presente investigación, cuyo objetivo fue analizar la influencia de la adición de
escoria de alto horno en diversas propiedades de un mortero hidráulico en comparación con un
mortero patrón, se empleó un enfoque descriptivo para identificar características y tendencias
en el comportamiento del mortero. A través del uso de un método de investigación hipotéticodeductivo,
se
partió
de
hipótesis
sobre
la
variación
de
propiedades
físico-mecánicas
debido
a
la
adición
de escoria de alto horno. El diseño de la investigación se clasificó como cuasiexperimental,
ya
que
se manipuló
deliberadamente
una
variable
independiente,
en
este
caso,
la
cantidad
de
escoria
añadida
al
mortero,
para
observar
su
efecto
en
las
variables
dependientes.
Con
relación a la población de estudio, se consideraron dos poblaciones de muestras. La
población se registra mediante un conjunto de testigos de mortero de una resistencia nominal
de F’c: 125 kg-f/cm2 (5x5x5 cm y 4x4x16 cm) elaborado con agregados de la cantera Vicho y
Cunyac, escoria de alto horno. La muestra se describió detalladamente, comprendiendo 12
unidades muéstrales para el ensayo de flujo plástico; 04 unidades muéstrales para el ensayo de
tiempo de fraguado en intervalos de tiempo de 15 minutos; 112 unidades muéstrales para el
ensayo de resistencia a la compresión con adición de 15%, 20% y 25% en intervalos de tiempo
de (6, 12, 18, 24 horas y 7, 14, 28 días); y finalmente, 112 unidades muéstrales para el ensayo
de resistencia a la flexión con la misma adición de escoria en los mismos intervalos de tiempo
mencionados. | es_PE |
dc.description.abstract | The present investigation, whose objective was to analyze the influence of the addition
of blast furnace slag on various properties of a hydraulic mortar in comparison with a standard
mortar, employed a descriptive approach to identify characteristics and trends in the behavior
of the mortar. Through the use of a hypothetico-deductive research method, hypotheses on the
variation of physical-mechanical properties due to the addition of blast furnace slag were
hypothesized. The research design was classified as quasi-experimental, since an independent
variable, in this case, the amount of slag added to the mortar, was deliberately manipulated to
observe its effect on the dependent variables. Regarding the study population, two sample
populations were considered. The population is recorded by a set of samples of mortar with a
nominal strength of F'c: 125 kg-f/cm2 (5x5x5 cm and 4x4x16 cm) made with aggregates from
the Vicho and Cunyac quarries, blast furnace slag. The sample was described in detail,
comprising 12 sample units for the plastic flow test; 04 sample units for the setting time test at
time intervals of 15 minutes; 112 sample units for the compressive strength test with 15%, 20%
and 25% addition at time intervals of (6, 12, 18, 24 hours and 7, 14, 28 days); and finally, 112
sample units for the flexural strength test with the same slag addition at the same time intervals
mentioned above. | en_US |
dc.format | application/pdf | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Andina del Cusco | es_PE |
dc.rights | info:eu-repo/semantics/restrictedAccess | es_PE |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | es_PE |
dc.subject | Mortero hidráulico | es_PE |
dc.subject | Escoria de alto horno | es_PE |
dc.subject | Tiempo de fraguado | es_PE |
dc.subject | Resistencia a la compresión | es_PE |
dc.title | Influencia de la adición de escoria de alto horno en el flujo, tiempo de fraguado, resistencia a la compresión y resistencia a la flexión de un mortero hidráulico, Cusco – 2023 | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.name | Ingeniero Civil | es_PE |
thesis.degree.grantor | Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura | es_PE |
thesis.degree.discipline | Ingeniería Civil | es_PE |
dc.publisher.country | PE | es_PE |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.01.01 | es_PE |
renati.advisor.dni | 44982950 | |
renati.advisor.orcid | https://orcid.org/0000-0002-7793-8844 | es_PE |
renati.author.dni | 73639249 | |
renati.discipline | 732016 | es_PE |
renati.juror | Gonzalez Mamany, Nico Yheison | |
renati.juror | Ascue Escalante, Kildare Jussety | |
renati.juror | Alvarez Espinoza, Jorge | |
renati.juror | Aguilar Huertas, José Ronald | |
renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | es_PE |
renati.type | https://purl.org/pe-repo/renati/type#tesis | es_PE |
dc.description.lineadeinvestigacion | Ciencia y tecnología de materiales e insumos en ingeniería. | es_PE |