dc.description.abstract | El agua es un recurso indispensable y su disponibilidad en la ciudad del Cusco no es
abundante las proyecciones indican que seguirá la emergencia por déficit del recurso hídrico. Por
lo cual, es importante tomar medidas para ahorrar este recurso en las industrias que consumen
grandes cantidades de agua, como es el caso de la industria de la construcción para la elaboración
de concreto y así lograr un desarrollo sostenible.
Es por ello, que este estudio se concentra en analizar las propiedades del concreto elaborado
con agua tratada de la PTAR San Jerónimo, en la provincia del Cusco, utilizando el método
Hipotético – Deductivo. Con este propósito, se fabricaron un total de 50 muestras de briquetas de
concreto con el fin de evaluar su desarrollo en términos de resistencia a la compresión. Estas
muestras se dividieron en 2 grupos: 25 briquetas de concreto convencional y 25 briquetas de
concreto utilizando agua tratada suministrada por la PTAR San Jerónimo. Las pruebas de
compresión se llevaron a cabo a los 3, 5, 7, 14 y 28 días de edad del concreto. Los resultados
revelaron que el concreto fabricado con agua tratada alcanzó una resistencia a la compresión de
229.68 kg/cm2 a los 28 días. Lo que significa que este concreto cumple con el 90 % de resistencia
respecto al concreto patrón. Por otro lado, la consistencia del concreto se midió de acuerdo con la
NTP 339.035, el concreto elaborado con agua tratada obtuvo un asentamiento de 3.28 pulgadas.
Lo que se interpreta que este concreto cumple con el rango de asentamiento. Así mismo, durante
la evaluación del tiempo de fraguado mediante la resistencia a la penetración, se determinó que el
concreto experimental logró cumplir con los requisitos de la NTP 339.088, al registrar un tiempo
de fraguado inicial de 06 horas y 14 minutos, así como un tiempo de fraguado final de 08 horas y
08 minutos, ambos tiempos están dentro de la variación de tiempo aceptable respecto al concreto patrón. Se concluyo que el concreto elaborado con agua tratada de la PTAR San Jerónimo cumple
con las propiedades físicas y mecánicas establecidas en la NTP 339.088. | es_PE |
dc.description.abstract | Water is an indispensable resource and its availability in the city of Cusco is not abundant.
Projections indicate that the emergency due to a deficit of water resources will continue. Therefore,
it is important to take measures to save this resource in industries that consume large amounts of
water, such as the construction industry for the production of concrete, and thus achieve sustainable
development.
For this reason, this study focuses on analyzing the properties of concrete made with treated
water from the San Jerónimo WWTP, in the province of Cusco, using the Hypothetical – Deductive
method. For this purpose, a total of 50 samples of concrete briquettes were manufactured in order
to evaluate their development in terms of compressive strength. These samples were divided into
2 groups: 25 conventional concrete briquettes and 25 concrete briquettes using treated water
supplied by the San Jerónimo WWTP. Compression tests were carried out at 3, 5, 7, 14 and 28
days of concrete age. The results revealed that the concrete manufactured with treated water
reached a compressive strength of 229.68 kg/cm2 after 28 days. Which means that this concrete
meets 90% resistance compared to the standard concrete. On the other hand, the consistency of the
concrete was measured according to NTP 339.035, the concrete made with treated water obtained
a slump of 3.28 inches. What is interpreted is that this concrete meets the slump range. Likewise,
during the evaluation of the setting time through penetration resistance, it was determined that the
experimental concrete managed to comply with the requirements of NTP 339,088, by recording
an initial setting time of 06 hours and 14 minutes, as well as a final setting time of 08 hours and
08 minutes, both times are within the acceptable time variation with respect to the standard
concrete. It was concluded that the concrete made with treated water from the San Jerónimo
WWTP complies with the physical and mechanical properties established in NTP 339,088. | en_US |
dc.format | application/pdf | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Andina del Cusco | es_PE |
dc.rights | info:eu-repo/semantics/restrictedAccess | es_PE |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | es_PE |
dc.subject | Agua tratada | es_PE |
dc.subject | San Jerónimo | es_PE |
dc.subject | Resistencia a la compresión | es_PE |
dc.title | Análisis de la influencia del agua tratada de la planta de tratamiento de aguas residuales San Jerónimo sobre las propiedades físico - mecánicas del concreto f'c 210 kg/cm2 en la ciudad del Cusco – 2023 | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.name | Ingeniero Civil | es_PE |
thesis.degree.grantor | Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura | es_PE |
thesis.degree.discipline | Ingeniería Civil | es_PE |
dc.publisher.country | PE | es_PE |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.01.01 | es_PE |
renati.advisor.dni | 46086133 | |
renati.advisor.orcid | https://orcid.org/0000-0002-3510-5043 | es_PE |
renati.author.dni | 70576531 | |
renati.discipline | 732016 | es_PE |
renati.juror | Gil Rodríguez, Carmen Cecilia | |
renati.juror | Gonzalez Mamany, Nico Yheison | |
renati.juror | Mendoza Escalante, Camilo | |
renati.juror | Oviedo Mena, Gabriela | |
renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | es_PE |
renati.type | https://purl.org/pe-repo/renati/type#tesis | es_PE |