dc.description.abstract | RESUMEN
Esta investigación se propuso con el objetivo de determinar la influencia del curado con
vapor frente a diferentes tipos de curado en la resistencia del concreto f’c=280 kg/cm2
modificado con fibras de policloruro de vinilo (PVC) y virutas de acero; el cual presentó un
enfoque cuantitativo para el cual se obtuvieron resultados a través de cálculos numéricos y
exactos. La muestra tomada para este estudio comprende 144 briquetas que constituyen el
conjunto de briquetas de concreto, de las cuales 36 briquetas tienen modificaciones con virutas
de acero que contienen 10% en peso del agregado fino; lo que crea una mayor resistencia a la
compresión y al corte debido a ciertas propiedades del acero aún presente en las virutas, y 36
briquetas tienen modificaciones con fibras de policloruro de vinilo (PVC) con una fracción en
volumen del 10% del agregado fino; lo que cambió la consistencia de la mezcla, redujo el
agrietamiento y la contracción por secado y aumentó la tenacidad; En este sentido, se evalúa la
resistencia a la compresión de las briquetas en el periodo de 07, 28 días; como lo menciona la
teoría que se refiere a la evaluación de la resistencia a la compresión, la cual indica que en este
período se logra la resistencia para la que está diseñado el concreto; y en el periodo de 50 días
para evaluar la variación de la resistencia a la compresión y definir la mejor combinación de un
método de curado para cada tipo de concreto evaluado. concluyendo que el curado con vapor
es el mejor método de curado en comparación con otros métodos de curado, lo que aumenta
significativamente la resistencia a la compresión de las briquetas de concreto, pero este método
de curado no es aplicable al concreto modificado con virutas de acero. ya que la resistencia
obtenida disminuye debido a la corrosión del acero, en el concreto modificado con fibras de
policloruro de vinilo (PVC) se observó un aumento de resistencia la cual se asemeja, pero no
supera los resultados de la muestra del concreto f’c=280 kg/cm2. | es_PE |
dc.description.abstract | ABSTRACT
This research aimed to determine the influence of steam curing compared to different
types of curing on the strength of concrete f'c=280 kg/cm2 modified with polyvinyl chloride
(PVC) fibers and steel chips. The study used a quantitative approach, obtaining results through
numerical and exact calculations. The sample for this study consisted of 144 concrete
briquettes, of which 36 briquettes were modified with steel chips containing 10% by weight of
fine aggregate. This modification increased the compressive and shear strength due to certain
properties of the steel still present in the chips. Additionally, 36 briquettes were modified with
PVC fibers with a 10% volume fraction of fine aggregate. This changed the consistency of the
mixture, reduced cracking and drying shrinkage, and increased toughness. In this regard, the
compressive strength of the briquettes was evaluated at 07 and 28 days, as these periods are
considered to achieve the design strength of the concrete. The compressive strength variation
was also evaluated at 50 days to determine the best curing method for each type of concrete.
The study concluded that steam curing is the best curing method compared to other methods,
significantly increasing the compressive strength of the concrete briquettes. However, this
curing method is not applicable to concrete modified with steel chips, as the obtained strength
decreases due to steel corrosion. On the other hand, the concrete modified with PVC fibers
showed an increase in strength, although it did not surpass the results of the f'c=280 kg/cm2
concrete sample. | en_US |
dc.format | application/pdf | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Andina del Cusco | es_PE |
dc.rights | info:eu-repo/semantics/openAccess | es_PE |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | es_PE |
dc.subject | Curado a vapor | es_PE |
dc.subject | Resistencia de un concreto | es_PE |
dc.subject | Virutas de acero | es_PE |
dc.title | Determinación de la influencia del curado a vapor frente a los diferentes tipos de curado en la resistencia de un concreto con policloruro de vinilo (PVC) y con acero, Cusco 2022 | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.name | Ingeniero Civil | es_PE |
thesis.degree.grantor | Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura | es_PE |
thesis.degree.discipline | Ingeniería Civil | es_PE |
dc.publisher.country | PE | es_PE |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.01.01 | es_PE |
renati.advisor.dni | 23807993 | |
renati.advisor.orcid | https://orcid.org/0000-0001-6891-6902 | es_PE |
renati.author.dni | 73328852 | |
renati.author.dni | 77798539 | |
renati.discipline | 732016 | es_PE |
renati.juror | Salas Fortón, Edson Julio | |
renati.juror | Ascue Escalante, Kildare Jussety | |
renati.juror | Alvarez Espinoza, Jorge | |
renati.juror | Tagle Sanchez, Raul | |
renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | es_PE |
renati.type | https://purl.org/pe-repo/renati/type#tesis | es_PE |