Evaluación comparativa del tiempo de fraguado, expansión potencial y la resistencia a la compresión del mortero de cemento, elaborado con puzolana de la cantera de Raqchi y cemento portland tipo I con respecto al cemento portland tipo IP.
View/ Open
Date
2015-09-11Author
Carrasco Flores, Nixon Nicanor
Quintanilla Cuellar, Miguel Angel
Advisor
Salas Fortón, Edson Julio
Metadata
Show full item recordAbstract
En la presente tesis se realizó la evaluación comparativa del mortero de cemento tipo I con diferentes porcentajes de puzolana de la zona de Raqchi, con respecto al cemento Pórtland tipo IP, realizando distintos ensayos, todos respetando las Normas Técnicas peruanas y ecuatorianas correspondientes al tipo de ensayo que se realizaron.
Primeramente se evaluó la resistencia a la compresión de los morteros de cemento tipo I con diferentes porcentajes de puzolana de la zona de Raqchi, así como de cemento Pórtland tipo IP, mediante cubos de 5cm (2”) de lado, sometidos a una fuerza constante de compresión en los cuales se cumplieron con la NTP. 334.051, concluyendo que a los 28 días de edad de los especímenes, los cuales fueron hechos desde un 15% hasta un 40% de puzolana , el mortero elaborado con cemento Pórtland tipo I y un 25% de puzolana nos brinda la mejor resistencia con un incremento de 2.90% más que el mortero patrón elaborado con cemento Pórtland tipo IP.
También se determinó el tiempo de fraguado de los morteros de cemento, de cemento tipo I con diferentes porcentajes de puzolana de la zona de Raqchi, así como de cemento Pórtland tipo IP, mediante el aparato de Vicat cumpliendo con las especificaciones dadas en la NTP. 334.090 y siguiendo el procedimientos de la NTP 334.006, nos dieron como resultado que:el tiempo promedio de fraguado inicial mínimo fue de 169.80 minutos (cemento Pórtland tipo I) y en tiempo de fraguado promedio máximo fue de 365.00 minutos o 6.08 horas (cemento Pórtland tipo I + 40% de puzolana), los cuales se encuentran dentro de los parámetros establecidos por la NTP. 334.090 (tabla 3 – Requisitos Físicos, pag.16) de no memos de 45 minutos para el fraguado inicial y no mayor de 7 horas (420 minutos).
Finalmente se analizó la expansión potencial de los morteros de cemento tipo I con diferentes porcentajes de puzolana de la zona de Raqchi, así como de cemento Portland tipo IP, los cuales fueron expuestos a sulfatos, teniendo como resultados que las muestras con el cemento tipo IP, tipo I y los adicionados con los diferentes porcentajes de la puzolana de Raqchi se expanden entre 0.1081% y 0.1148% en el eje horizontal, 0.1017% y 0.1072% en el eje vertical y 0.1030% y 0.1086% en su longitud, los cuales están dentro de los parámetros permitidos de acuerdo a la NTE INEN 0202, el cual es equivalente a la ASTM C452-06. In the present thesis we made a comparative evaluation of the Type I
cement mortar with different percentages of pozzolana from the zone of
Raqchi, comparing it to the Type IP Portland Cement. We performed
various tests, all within conformity to Peruvian Technical Norms (NTP).
We first evaluated the Type I cement mortars with regard to their
resistance to compression, testing the Portland Type IP cement as a
control. We used 5 cm (2”) cubes subjected to a constant compression
force in conformity with NTP
334.051. After 28 days, of the specimens which were made with 15% to
40% puzzolana, the mortar made with 25% puzzolana yields the best
resistance with an increment of 2.90% more resistance than the control
mortar made with Portland Type IP cement.
The setting time of cement mortars , cement type I with different
percentages of pozzolan area Raqchi and IP type of Portland cement was
also determined by the Vicat apparatus complying with the specifications
given in the NTP . 334 090 and following the procedures of the NTP 334
006 , we got the result that : the average time minimum initial set was
169.80 minutes ( Portland cement type I) and time of maximum average
setting was 365.00 minutes or 6.08 hours ( Portland cement type I + 40 %
pozzolan ) , which are within the parameters set by the NTP . 334 090
(Table 3 - Physical Requirements p.16 ) non memos 45 minutes for the
initial setting and not more than 7 hours (420 minutes).
Finally, we analyzed the potential expansion of the Type I and Portland
Type IP mortars, exposing each mortar to sulfates. We found that the
samples of the Type IP, Type I, and the Type I with added puzzolana
from Raqchi expand between 0.1081% and 0.1148% on the horizontal
axis (width); 0.1017% and 0.1072% on the vertical axis (height); and
0.1030% and 0.1086% in length. Which are within the allowed
parameters according to NTE INEN 0202 , which is equivalent to the
ASTM C452-06 .
Collections
Related items
Showing items related by title, author, creator and subject.
-
Evaluación comparativa de la fluidez, peso específico, adherencia, resistencia a la compresión y flexión de mortero elaborado con cemento Portland Tipo IP y tipo I con el reemplazo del cemento Portland Tipo I por Puzolana de la cantera de Ccocha - San Pedro Sicuani - Cusco.
Chillihuani Ccorimanya, Nelson; Percca Ccoaquira, Americo (Universidad Andina del Cusco, 2016)Acceso restringidoEn la presente tesis se realizó la evaluación comparativa del mortero de cemento Tipo I y mortero con el reemplazo del cemento Portland Tipo I en peso por puzolana de la cantera de Ccocha, con respecto al cemento Pórtland ... -
Análisis de las propiedades físico-mecánicas de las unidades de albañilería de suelo cemento fabricadas con arena de la cantera de Vicho, suelo de la zona ladrillera de San Jerónimo y cemento portland tipo IP.
Quiroz Gonzales, Juan de Dios (Universidad Andina del Cusco, 2015-09-08)Acceso restringidoLa presente investigación fue orientada al estudio de las propiedades físico- mecánicas de las unidades de albañilería de suelo cemento fabricadas con arena de la cantera de Vicho, suelo de la zona ladrillera de San Jerónimo ... -
Análisis comparativo de las propiedades físico-mecánicas y costos de material de un cemento portland tipo ip respecto a un cemento parcialmente adicionado con cenizas de rastrojo de maíz evaluados según los criterios de la ntp 334.090 en la provincia del Cusco 2018.
Heredia Ortiz, Maria Luisa; Leverenz Fernández, Marcia (Universidad Andina del Cusco, 2018-12-14)Acceso restringidoLa presente investigación enmarcó en la ciudad del Cusco y tiene como objetivo principal analizar las propiedades físico-mecánicas de un cemento adicionado con 5%, 7% y 10% de cenizas de rastrojo de maíz comparado con un ...