dc.description.abstract | La presente tesis de investigación estudió las propiedades físico – mecánicas de un
mortero patrón, sustituyendo neumáticos fuera de uso (NFU) en porcentajes de 10%, 20% y
30% con respecto al peso de la arena fina de la cantera de Cunyac. La propiedad física
investigada fue: el ensayo de fluidez; mientras que las propiedades mecánicas evaluadas fueron:
los ensayos de resistencia a compresión, flexión y adherencia. El mortero se preparó con
agregados finos prevenientes de la cantera Cunyac y Cemento portland tipo IP. La fluidez se
determina en estado fresco del mortero y resistencia a la compresión, flexión y adherencia
fueron evaluadas a los 7, 14 y 28 días de curado. Para la preparación de muestras, ejecución de
ensayos y análisis de datos se utilizaron normas técnicas peruanas (NTP334.051, 2006 y
NTP.334.057, 2014), la Norma Mexicana (NMX-C-303-1986) y la norma Guatemalteca
(NORMA COGUANOR NTG 41051 h7). Los especímenes fueron: Dados de mortero
(Dimensiones: 5cm x 5cm x 5cm) para ensayo de resistencia a compresión, prismas de mortero
(Dimensiones: 10cm x10cm x40cm) para ensayo de resistencia a flexión, ladrillos cruzados con
mortero de pega para ensayo de adherencia y mortero en estado fresco para ensayo de fluidez.
Los especímenes con sustitución, son añadidos con neumáticos fuera de uso molidos (NFU) al
10%, 20% y 30% con respecto al peso de la arena fina. La población estuvo compuesta por 60
dados, 60 prismas de mortero, 60 ladrillos cruzados y 20 muestras de mortero para fluidez. La
dosificación empleada fue Agua: 0.562, Cemento: 1, Arena: 1.676. Analizando los resultados,
la resistencia a la compresión, flexión y fluidez son inversamente proporcionales al incremento
de NFU molido en reemplazo de la arena fina del mortero de revestimiento. El mortero con 10%
de NFU tiene un incremento de 1.41% en la adherencia y se encuentra dentro del rango admitido de la flexión. Se observó roturas frágiles en las muestras de mortero patrón y roturas dúctiles en
muestras con NFU añadido en los ensayos de compresión y flexión. | es_PE |
dc.description.abstract | This research thesis studied the physical-mechanical properties of a standard mortar,
substituting used tires (NFU) in percentages of 10%, 20%, and 30% by weight of the fine sand
from the Cunyac quarry. The physical property investigated was the flow test, while the
mechanical properties evaluated were the compression, flexural, and adhesion tests. The mortar
was prepared with fine aggregates from the Cunyac quarry and type IP Portland cement. Flow
was determined in the fresh state of the mortar, and compression, flexural, and adhesion
resistance were evaluated at 7, 14, and 28 days of curing. Peruvian technical standards
(NTP334.051, 2006 and NTP.334.057, 2014), the Mexican Standard (NMX-C-303-1986), and
the Guatemalan Standard (NORMA COGUANOR NTG 41051 h7) were used for the
preparation of samples, execution of tests, and data analysis. The specimens were: mortar cubes
(Dimensions: 5cm x 5cm x 5cm) for compression test, mortar prisms (Dimensions: 10cm x10cm
x40cm) for flexural strength test, cross-brick with mortar for adhesion test, and fresh mortar for
flow test. The specimens with substitution were added with ground used tires (NFU) at 10%,
20%, and 30% by weight of fine sand. The population consisted of 60 mortar cubes, 60 mortar
prisms, 60 cross-bricks, and 20 mortar samples for flow. The dosing used was Water: 0.562,
Cement: 1, Sand: 1.676. Analyzing the results, compression, flexural strength, and flow were
inversely proportional to the increase in ground NFU replacing the fine sand in the coating
mortar. The mortar with 10% of NFU has a 1.41% increase in adhesion and is within the
accepted range for flexion. Fractures were observed in the standard mortar samples, while
ductile fractures were observed in samples with added NFU in compression and flexural tests. | en_US |
dc.format | application/pdf | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Andina del Cusco | es_PE |
dc.rights | info:eu-repo/semantics/restrictedAccess | es_PE |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | es_PE |
dc.subject | Mortero | es_PE |
dc.subject | Resistencia a la compresión | es_PE |
dc.subject | Flexión | es_PE |
dc.subject | Adherencia | es_PE |
dc.title | Análisis comparativo de las propiedades físico - mecánicas de un mortero patrón para revestimiento, sustituyendo neumáticos fuera de uso (NFU) molidos en porcentajes de 10%, 20% y 30% con respecto al peso de la arena fina de la cantera de Cunyac, Cusco 2022 | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.name | Ingeniero Civil | es_PE |
thesis.degree.grantor | Universidad Andina del Cusco. Facultad de Ingeniería y Arquitectura | es_PE |
thesis.degree.discipline | Ingeniería Civil | es_PE |
dc.publisher.country | PE | es_PE |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.01.00 | es_PE |
renati.advisor.dni | 45246758 | |
renati.advisor.orcid | https://orcid.org/0000-0003-1309-4280 | es_PE |
renati.author.dni | 72743832 | |
renati.author.dni | 70301600 | |
renati.discipline | 732016 | es_PE |
renati.juror | Calderon Gonzalez, Werner Alfonso | |
renati.juror | Rios Ravelo, José Luis | |
renati.juror | Gil Rodriguez, Carmen Cecilia | |
renati.juror | Alvarez Monterola, Walter Roberto | |
renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | es_PE |
renati.type | https://purl.org/pe-repo/renati/type#tesis | es_PE |