    Análisis comparativo de propiedades físicas y mecánicas del concreto celular elaborado con el componente lauril sulfato de sodio respecto a un concreto tradicional f`c=210 kg/cm2 elaborado con agregado de las canteras vichos, mina Roja y Cunyac.

    Thumbnail
    View/Open
    RESUMEN.pdf (529.7Kb)
    Date
    2017-12-13
    Author
    Chávez Palomino, Leornardo Germán
    Salluca Rodríguez, Marlon Javier
    Advisor
    Enciso Boluarte, Henry
    Metadata
    Show full item record
    Abstract
    El presente trabajo de investigación se desarrolló en la ciudad de Cusco, donde se evaluó la resistencia a la compresión, resistencia a la flexión y el peso específico del concreto elaborado con el componente químico “LAURIL SULFATO DE SODIO” (LSS); este componente presente en productos como jabones, detergentes y otros productos de limpieza que producen burbujas así como también en aditivos incorporadores de aire para concreto que se emplea en climas fríos donde se dan los fenómenos de hielo-deshielo en el concreto. Para comprobar los resultados se procedió a la elaboración de briquetas cilíndricas de concreto como también viguetas y cubos de concreto; con resistencia de diseño 210 kg/cm2; con tiempos de curado de 7, 14 y 28 días en porcentajes de LSS: 0.02%, 0.05%, 0.08% y 0.12%; En los resultados de la investigación se pudo determinar que el empleo del componente LSS como aditivo incorporador de aire incrementa la resistencia a la compresión inicial y final en los porcentajes de 0.02% y 0.05% y reduce en los porcentajes de 0.08% y 0.12%; así como también se determinó que la resistencia a la flexión se incrementó en los porcentaje 0.02% y 0.05% de LSS y disminuye en los porcentajes de 0.08% y 0.12% de LSS por último se determinó que el peso específico del concreto modificado disminuye inversamente proporcional al porcentaje de LSS que se emplee, todos estos resultados fueron comparados especto al concreto elaborado sin modificar.
     
    This research work was developed in the city of Cusco, where the resistance to compression, resistance to bending and the specific weight of concrete made with the chemical component “LAURIL SODIUM SULFATE“ (LSS); this component is present in products such as soaps, detergents and other cleaning products that produce bubbles as well as in air-entraining additives for concrete that is used in cold climates where the ice-thaw phenomena occur in the concrete. To verify the results, concrete cylindrical specimens were produced, as well as joists and concrete cubes; with design strength of 210 kg / cm2; with cure times of 7, 14 and 28 days and with LSS percentages of 0.02%, 0.05%, 0.08% and 0.12%; In the results of the investigation it was determined that the use of the LSS component as an airentraining additive increases the initial and final compression resistance in the percentages of 0.02% and 0.05% and reduces in the percentages of 0.08% and 0.12%; as well as it was determined that the flexural strength was increased in the percentage 0.02% and 0.05% of LSS and decreases in the percentages of 0.08% and 0.12% of LSS finally determined that the specific weight of the modified concrete decreases inversely proportional to the percentage of LSS that is used, all these results were compared with respect to the concrete produced without modification.
     
    URI
    https://hdl.handle.net/20.500.12557/1453
    Collections
    • Escuela Profesional de Ingeniería Civil [469]

    Contacto:  repositorio.digital@uandina.edu.pe

     

     

    Documentos de Interés
    AutorizaciónSoftware de similitudNormativas y/o DirectivasRegistro ORCIDGuías

    Browse

    All of DSpaceCommunities & CollectionsBy Issue DateAuthorsxmlui.ArtifactBrowser.Navigation.browse_advisorTitlesSubjectsThis CollectionBy Issue DateAuthorsxmlui.ArtifactBrowser.Navigation.browse_advisorTitlesSubjects

    My Account

    LoginRegister

    Contacto:  repositorio.digital@uandina.edu.pe