dc.description.abstract | El presente estudio de investigación fue realizado con el objetivo de evaluar la
microfiltración en incrustaciones inlay de resina cementadas con resina termo
modificada Amelogen (ultradent) y cemento dual variolink (ivoclar vivadent) a las 24
horas y a los 7 días, Universidad Andina del Cusco – 2019.
La metodología utilizada se realizó mediante un estudio comparativo,
cuasiexperimental. La muestra fue dada por 40 piezas dentarias premolares, con
preparaciones inlay que fueron separadas en 2 grupos de estudio: 1° Grupo. - 20
piezas dentarias con resina termo modificada Amelogen (ultradent), 2° Grupo. - 20
piezas dentarias con cemento dual variolink N (ivoclar vivadent).
Las muestras fueron sometidas a termociclado en azul de metileno al 1% con la
finalidad de conseguir cierto envejecimiento de las piezas dentarias. Luego de 24
horas se procedió a retirar 10 piezas dentarias de cada grupo y el resto fue retirado
a los 7 días. Para luego ser observadas en el microscopio estereoscopio Los
resultados de la microfiltración en incrustaciones inlay de resina cementada con
resina termo modificada Amelogen (ultradent) y cemento dual vario link (ivoclar
vivadent) fue a las 24 horas fue mayor para el cemento dual en relación a la resina
termo modificada que tuvo significancia p= 0.044 (p<0.05). A los 7 días la
microfiltración fue mayor para el cemento dual en relación a la resina termo
modificada esta fue significativa p=0.006 (p<0.05). La microfiltración en
incrustaciones inlay de resina cementadas con resina termo modificada Amelogen
(ultradent) fue menor a los 7 días en relación a las 24 horas. Y la resina con cemento
dual variolink (ivoclar vivadent) fue igual a las 24 horas y a los 7 días. | es_PE |
dc.description.abstract | The present research study was carried out with the objective of evaluating MICRO-
Leakage in cemented resin inlays with Amelogen thermo-modified resin (ultradent)
and variolink dual cement (Ivoclar vivadent) at 24 hours and 7 days, Universidad
Andina del Cusco – 2019.
The methodology used was carried out through a comparative, quasi-experimental
study. The sample was given by 40 premolar teeth, with inlay preparations that were
separated into 2 study groups: 1st Group. - 20 teeth with Amelogen thermo-modified
resin (ultradent), 2nd Group. - 20 dental pieces with variolink N dual cement (Ivoclar
vivadent). The samples were subjected to thermocycling in 1% methylene blue in
order to achieve a certain aging of the dental pieces. After 24 hours, 10 teeth were
removed from each group and the rest were removed after 7 days. To then be
observed in the stereoscopic microscope. The results of microleakage in resin inlays
cemented with thermo-modified resin Amelogen (ultradent) and variolink dual
cement (ivoclar vivadent) was at 24 hours higher for the dual cement in relation to
the thermo-modified resin, which had significance p = 0.044 (p<0.05). At 7 days, the
microleakage was higher for the dual cement in relation to the thermo-modified
resin, this was significant p=0.006 (p<0.05). Microleakage in resin inlays cemented
with Amelogen thermo-modified resin (ultradent) was lower at 7 days compared to
24 hours. And the resin with variolink dual cement (ivoclar vivadent) was the same
at 24 hours and 7 days. | en_US |
dc.format | application/pdf | es_PE |
dc.language.iso | spa | es_PE |
dc.publisher | Universidad Andina del Cusco | es_PE |
dc.rights | info:eu-repo/semantics/restrictedAccess | es_PE |
dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | es_PE |
dc.subject | Microfiltración | es_PE |
dc.subject | Resina termomodificada | es_PE |
dc.title | Estudio comparativo in vitro de la microfiltración en incrustaciones Inlay de resina cementadas con resina termomodificada amelogen (ultradent) y cemento dual variolink N (ivoclar vivadent) Universidad Andina del Cusco – 2019 | es_PE |
dc.type | info:eu-repo/semantics/bachelorThesis | es_PE |
thesis.degree.name | Cirujana Dentista | es_PE |
thesis.degree.grantor | Universidad Andina del Cusco. Facultad de Ciencias de la Salud | es_PE |
thesis.degree.discipline | Estomatología | es_PE |
dc.publisher.country | PE | es_PE |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#3.02.14 | es_PE |
renati.advisor.dni | 29335747 | |
renati.advisor.orcid | https://orcid.org/0000-0002-1974-8321 | es_PE |
renati.author.dni | 46626268 | |
renati.discipline | 911016 | es_PE |
renati.juror | Arenas Fernández Dávila, Jesús Alejandro | |
renati.juror | Gamero Huarcaya, Valery Kimiyo | |
renati.juror | Rosas Cisneros, Hugo Leoncio | |
renati.juror | Urbiola Camacho, Rudyard Jesús | |
renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | es_PE |
renati.type | https://purl.org/pe-repo/renati/type#tesis | es_PE |